Periwinkle blue liquid glaze SOL03/106
Without lead
Firing temperature : 980-990°C
Blue celestial liquid glaze SOL03/105
Without lead
Firing temperature : 980-990°C
Ultramarine blue liquid glaze SOL03/103
Without lead
Firing temperature : 980-990°C
White mat liquid glaze SOL02/024
Without lead
Firing temperature : 980-990°C
Shinny white liquid glaze SOL02/019
Without lead
Firing temperature : 980-990°C
Transparent glaze SOL01/021
Without lead
Firing temperature : 950-980°C
TRANSPARENT MATE LIQUID GLAZE WITHOUTLEAD SOL01/009L
Transparent mate liquid glaze SOL01/009L
Transparent glossed glaze SOL01/009
With lead
Firing temperature : 980-1020°C
Transparent crackled glaze SOL01/004L
Without lead
Firing temperature : 980-990°C
Transparent crackled glaze SOL01/004
Without lead
Firing temperature : 1000-1300°C
Coefficient of dilatation: 101
Antique ivory white enamel - SIGLO XVIII
Opaque white zircon enamel.
For the enameling of earthenware and tiles which one wants to obtain an "antique" aspect.
Admits decoration.
The firing temperature varies between 950-1000ºC.
Ivory white enamel - SIGLO XV
Opaque glossy white enamel.
This is an enamel studied to imitate antique white enamels which have a slightly yellowish (dirty white) tone.
We recommend using the special color series for decorating SIGLO XIII-type pieces.
Can be used indifferently on white and red paste.
The recommended firing temperature varies between 950-1000°C.
Crystallized brown S3A
Lustres glazer with lead
Temperature for firing : 850-990°C
Presence of lead. Use only for decorative products
Base R2 - RAKU2
Glaze for Raku
Temperature of firing : 800-900°C
Groupe I
Without lead
Base R1 - RAKU1
Glaze for Raku
Temperature of firing : 800-900°C
Groupe I
Without lead
Raku glazes especially elaborated for Raku technic.
Made up of 5 basis. Usable in bath glaze, with spray gun or with brush.
Also proposed 3 sinters of basis.
The medium has to be refractory.
Temperature of firing : 800-900°C
Groupe III -Presence of lead.
Raku glazes especially elaborated for Raku technic.
Made up of 5 basis. Usable in bath glaze, with spray gun or with brush.
Also proposed 3 sinters of basis.
The medium has to be refractory.
Temperature of firing : 800-900°C
Presence of lead. Do not use for alimentary products. Only for decorative products
Raku glazes especially elaborated for Raku technic.
Made up of 5 basis.
Usable in bath glaze, with spray gun or with brush.
Also proposed 3 sinters of basis.
The medium has to be refractory.
Advice :
Temperature of firing : 800-900°C
Coefficient of expansion: 104
Mentions :
Presence of lead. Do not use for alimentary products. Only for decorative products
Raku glazes especially elaborated for Raku technic.
Made up of 5 basis.
Usable in bath glaze, with spray gun or with brush.
Also proposed 3 sinters of basis.
The medium has to be refractory.
Advice:
Temperature of firing : 800-900°C
Mentions :
Presence of lead. Do not use for alimentary products. Only for decorative products
Brown lustre glaze R1003
With lead
Firing temperature : 960-1020°C
Transparent glaze - PR O
Composed of Frit.
Transparent varnished which has been specially studied for pieces of pottery which must contain food.
It adapts correctly both to popular earthenware (red clay) in double firing, as in single firing, because in its formulation, products are included which favor its adhesion to the soil.
It admits the addition of coloring oxides and in particular the natural ones (Cu, Co, Mn, Fe, ....).
It perfectly develops both underglaze colors and our range of colored engobes.
The firing temperature varies between 930-980ºC. At temperatures above 970ºC, kaolin or clay should be added.
Transparent lead-free powder enamel - PR99
Composed of Fritte.
For enamelling of white earthenware.
We can decorate under and on enamel.
Obtaining coloured enamels by adding dyes from the "P" series.
Firing temperature between 1000 and 1100ºC.
Bright white zircon enamel - PR 6303 F
Composed of Frit.
Bright opaque white enamel, lead free. Recommended for parts for food use.
For the enameling of ceramic pieces in red or white earth, especially those which must contain food.
Can be colored with natural oxides or calcined type P series. If the room must contain food, use lead-free dyes. The application can be done with a bath, brush, spray gun or screen printing.
Firing temperature between 1000-1020ºC where the enamel shows its best development.
Transparent glaze - PR500
Composed of Fritte.
Shiny transparent enamel without lead.
For enamelling of ceramic pieces in red or white clay.
Firing temperature between 950-1020ºC.
Transparent glaze - PR 47
Composed of Frit.
Shiny transparent enamel with a high amount of calcium.
Recommended as a base for producing colored enamels with coloring oxides compounds based on calcium, such as for example the base of (Cr, Sn, Ca).
Rutile base when looking for a lead enamel with a high melting viscosity which must be used at a temperature above 1000º C.
The firing temperature varies between 980-1050ºC.
Melting to lower the firing temperature - PR 32
Composed of Frit.
LEAD FREE CLEAR MELTING ENAMEL.
For the enameling of ceramic pieces in red or white clay.
Lead free fondant to add to enamels that need to increase fusibility.
Optimal firing temperature between 850-900ºC.
Glossy transparent enamel - PR233
Composed of Frit.
Glossy transparent enamel, lead free.
For glazing ceramic pottery pieces in red or white clay.
Firing temperature, between 950-1020ºC.
Bright white zircon enamel - PR23
Composed of Frit.
It is an enamel specially designed for pottery and tiling.
Admits decoration well.
The firing temperature varies between 950-1000ºC.