GLAZE

Transparent glaze - PR O

Composed of Frit.

Transparent varnished which has been specially studied for pieces of pottery which must contain food.

It adapts correctly both to popular earthenware (red clay) in double firing, as in single firing, because in its formulation, products are included which favor its adhesion to the soil.

It admits the addition of coloring oxides and in particular the natural ones (Cu, Co, Mn, Fe, ....).

It perfectly develops both underglaze colors and our range of colored engobes.

The firing temperature varies between 930-980ºC. At temperatures above 970ºC, kaolin or clay should be added.

Transparent lead-free powder enamel - PR99

Composed of Fritte.

For enamelling of white earthenware.

We can decorate under and on enamel.

Obtaining coloured enamels by adding dyes from the "P" series.

Firing temperature between 1000 and 1100ºC.

Bright white zircon enamel - PR 6303 F

Composed of Frit.

Bright opaque white enamel, lead free. Recommended for parts for food use.

For the enameling of ceramic pieces in red or white earth, especially those which must contain food.

Can be colored with natural oxides or calcined type P series. If the room must contain food, use lead-free dyes. The application can be done with a bath, brush, spray gun or screen printing.

Firing temperature between 1000-1020ºC where the enamel shows its best development.

Transparent glaze - PR500

Composed of Fritte.

Shiny transparent enamel without lead.

For enamelling of ceramic pieces in red or white clay.

Firing temperature between 950-1020ºC.

Transparent glaze - PR 47

Composed of Frit.

Shiny transparent enamel with a high amount of calcium.

Recommended as a base for producing colored enamels with coloring oxides compounds based on calcium, such as for example the base of (Cr, Sn, Ca).

Rutile base when looking for a lead enamel with a high melting viscosity which must be used at a temperature above 1000º C.

The firing temperature varies between 980-1050ºC.

Melting to lower the firing temperature - PR 32

Composed of Frit.

LEAD FREE CLEAR MELTING ENAMEL.

For the enameling of ceramic pieces in red or white clay.

Lead free fondant to add to enamels that need to increase fusibility.

Optimal firing temperature between 850-900ºC.

Glossy transparent enamel - PR233

Composed of Frit.

Glossy transparent enamel, lead free.

For glazing ceramic pottery pieces in red or white clay.

Firing temperature, between 950-1020ºC.

Bright white zircon enamel - PR23

Composed of Frit.

It is an enamel specially designed for pottery and tiling.

Admits decoration well.

The firing temperature varies between 950-1000ºC.

Transparent glaze - PR 211 B

Composed of Frit.

The firing temperature varies between 980-1020ºC.

Lead-free opaque white satin enamel - PR20 (PR20/N)

The firing temperature varies between 980-1100ºC.

Satin transparent glaze - PR17

Composed of Frit.

Clear satin lead-free enamel.

The firing temperature varies between 980-1050ºC.

Calco-alkaline glaze - PR 1440 (FR 10)

Composed of fritte.

Lead-free transparent enamel with relatively high expansion.

Application Ceramic product for enamelling of white and red clay pieces with an expansion superior to the standard.

Admit to the decoration.

The firing interval is between 940 and 1000ºC.