Bright yellow XP3053/T
Free of lead
GROUPE I
Temperature of firing : 930-1050°C
Coefficient of expansion: 55
Bright yellow XP3053
Free of lead
Temperature of firing : 980-1020°C
Coefficient of expansion: 55
Bright red XP3052/T
Free of lead
GROUPE I
Temperature of firing : 930-1050°C
Coefficient of expansion
Bright red XP3052
Free of lead
Temperature of firing : 980-1020°C
Coefficient of expansion: 55
Bright orange XP3051/T
Free of lead
GROUPE I
Temperature of firing : 930-1050°C
Coefficient of expansion: 55
Bright orange XP3051
Free of lead
Temperature of firing : 980-1020°C
Coefficient of expansion: 55
Bright oranged yellow XP3050/T
GROUPE I
Free of lead
Temperature of firing : 930-1050°C
Coefficient of expansion: 55
ENAMEL XP3050 BRIGHT ORANGE YELLOW OPAQUE LEAD FREE
Glaze Copper green XP3048
Groupe I
Firing temparature: 960-1050°C
Glaze Honey XP3043
Advice :
Temperature of firing : 930-980°C
Dilation coeff : 74
Mentions :
GROUPE I : Enamel without lead
Lead-free copper green enamel - XP 3025
For enamelling ceramic pieces in red clay or engobed.
Firing temperature between 980-1020°C.
Green - VR97
Groupe III
Firing temperature: 960-1050°C
Transparent glaze - TSP 2
Composed of Frit.
Clear crystalline lead free.
For enamelling ceramic parts.
Admits the addition of dyes with excellent color development.
Has a firing interval between 1020-1080ºC.
Transparent glaze SOL01/021
Without lead
Firing temperature : 950-980°C
Transparent glossed glaze SOL01/009
With lead
Firing temperature : 980-1020°C
Transparent crackled glaze SOL01/004
Without lead
Firing temperature : 1000-1300°C
Coefficient of dilatation: 101
Antique ivory white enamel - SIGLO XVIII
Opaque white zircon enamel.
For the enameling of earthenware and tiles which one wants to obtain an "antique" aspect.
Admits decoration.
The firing temperature varies between 950-1000ºC.
Ivory white enamel - SIGLO XV
Opaque glossy white enamel.
This is an enamel studied to imitate antique white enamels which have a slightly yellowish (dirty white) tone.
We recommend using the special color series for decorating SIGLO XIII-type pieces.
Can be used indifferently on white and red paste.
The recommended firing temperature varies between 950-1000°C.
Crystallized brown S3A
Lustres glazer with lead
Temperature for firing : 850-990°C
Presence of lead. Use only for decorative products
Brown lustre glaze R1003
With lead
Firing temperature : 960-1020°C
Transparent glaze - PR O
Composed of Frit.
Transparent varnished which has been specially studied for pieces of pottery which must contain food.
It adapts correctly both to popular earthenware (red clay) in double firing, as in single firing, because in its formulation, products are included which favor its adhesion to the soil.
It admits the addition of coloring oxides and in particular the natural ones (Cu, Co, Mn, Fe, ....).
It perfectly develops both underglaze colors and our range of colored engobes.
The firing temperature varies between 930-980ºC. At temperatures above 970ºC, kaolin or clay should be added.
Transparent lead-free powder enamel - PR99
Composed of Fritte.
For enamelling of white earthenware.
We can decorate under and on enamel.
Obtaining coloured enamels by adding dyes from the "P" series.
Firing temperature between 1000 and 1100ºC.
Bright white zircon enamel - PR 6303 F
Composed of Frit.
Bright opaque white enamel, lead free. Recommended for parts for food use.
For the enameling of ceramic pieces in red or white earth, especially those which must contain food.
Can be colored with natural oxides or calcined type P series. If the room must contain food, use lead-free dyes. The application can be done with a bath, brush, spray gun or screen printing.
Firing temperature between 1000-1020ºC where the enamel shows its best development.