Bright white zircon enamel - PR 6303 F
Composed of Frit.
Bright opaque white enamel, lead free. Recommended for parts for food use.
For the enameling of ceramic pieces in red or white earth, especially those which must contain food.
Can be colored with natural oxides or calcined type P series. If the room must contain food, use lead-free dyes. The application can be done with a bath, brush, spray gun or screen printing.
Firing temperature between 1000-1020ºC where the enamel shows its best development.
Transparent glaze - PR500
Composed of Fritte.
Shiny transparent enamel without lead.
For enamelling of ceramic pieces in red or white clay.
Firing temperature between 950-1020ºC.
Transparent glaze - PR 47
Composed of Frit.
Shiny transparent enamel with a high amount of calcium.
Recommended as a base for producing colored enamels with coloring oxides compounds based on calcium, such as for example the base of (Cr, Sn, Ca).
Rutile base when looking for a lead enamel with a high melting viscosity which must be used at a temperature above 1000º C.
The firing temperature varies between 980-1050ºC.
Melting to lower the firing temperature - PR 32
Composed of Frit.
LEAD FREE CLEAR MELTING ENAMEL.
For the enameling of ceramic pieces in red or white clay.
Lead free fondant to add to enamels that need to increase fusibility.
Optimal firing temperature between 850-900ºC.
Glossy transparent enamel - PR233
Composed of Frit.
Glossy transparent enamel, lead free.
For glazing ceramic pottery pieces in red or white clay.
Firing temperature, between 950-1020ºC.
Bright white zircon enamel - PR23
Composed of Frit.
It is an enamel specially designed for pottery and tiling.
Admits decoration well.
The firing temperature varies between 950-1000ºC.
Transparent glaze - PR 211 B
Composed of Frit.
The firing temperature varies between 980-1020ºC.
Lead-free opaque white satin enamel - PR20 (PR20/N)
The firing temperature varies between 980-1100ºC.
Satin transparent glaze - PR17
Composed of Frit.
Clear satin lead-free enamel.
The firing temperature varies between 980-1050ºC.
Calco-alkaline glaze - PR 1440 (FR 10)
Composed of fritte.
Lead-free transparent enamel with relatively high expansion.
Application Ceramic product for enamelling of white and red clay pieces with an expansion superior to the standard.
Admit to the decoration.
The firing interval is between 940 and 1000ºC.
Transparent boro calcium enamel - PR1430
Transparent and glossy enamel, lead-free.
Transparent expansion corrector enamel - PR14
It is a corrector, low dilatation.
Application Raw material in ceramics.
The use is very limited by its low expansion.
It can be added to certain enamels to reduce their dilatation.
Recommended firing temperature between 980-1050ºC.
Glossy white enamel - PR 125
Opaque white enamel.
For the enameling of ceramic pieces in white or red earth.
It can be applied both by dipping and spraying.
The recommended firing temperature is between 980-1000ºC.
White enamel for undercoat - PR 120 BB
Composed of Frit.
For glazed tiles on the bisqueware.
Then apply a thin layer of transparent enamel.
The firing temperature varies between 960-1000ºC.
Glossy white enamel - PR 115
Composed of Frit.
High gloss Opaque White enamel, low expansion.
Can be used with excellent results on tiles or red earthenware as well as white majolica.
The firing temperature varies between 1000-1080ºC.
Extra white zircon enamel - PR 112
Composed of Frit.
Lead-free Opaque White Enamel.
Slightly bluish white enamel, studied for food, decorative or sanitary ceramics by firing above 1100ºC, in single or double firing.
Recommended temperature, between 1050-1150ºC.
Transparent enamel - PR 1000 (FR 8)
Composed of frit.
Transparent, lead-free and very melting email.
Raw material in the ceramic industry.
This is a basis for the development of lead-free enamels.
Recommended firing temperature between 850-1000°C.
Mat white - PR08
With lead
Groupe II
Firing temperature: 980-1020°C
Coefficient of expansion: 58
WHITE IVORY ANTIC GLAZE - OPACANTIC
White ivory antique
Ref : OPACANTIC
Temperature of firing : 950-1050°C
Coeff Dilat 25-300°C: 62
Groupe II
With lead
Transparent glaze - NS20M
Composed of Frit.
Lead-free shiny transparent enamel.
For enamelling ceramic pieces in white clay.
Firing temperature between 980-1020ºC.
Black- N3320M/7 dur
GROUPE III
Firing temperature: 980-990°C
BLUE LUSTRE GLAZE N3303
Blue lustre N3303
Mono lead silicate enamel - MONOPB
Composed of Frit.
Transparent, shiny and melting enamel.
With lead.