Transparent glaze - PR 47
Composed of Frit.
Shiny transparent enamel with a high amount of calcium.
Recommended as a base for producing colored enamels with coloring oxides compounds based on calcium, such as for example the base of (Cr, Sn, Ca).
Rutile base when looking for a lead enamel with a high melting viscosity which must be used at a temperature above 1000º C.
The firing temperature varies between 980-1050ºC.
Melting to lower the firing temperature - PR 32
Composed of Frit.
LEAD FREE CLEAR MELTING ENAMEL.
For the enameling of ceramic pieces in red or white clay.
Lead free fondant to add to enamels that need to increase fusibility.
Optimal firing temperature between 850-900ºC.
Glossy transparent enamel - PR233
Composed of Frit.
Glossy transparent enamel, lead free.
For glazing ceramic pottery pieces in red or white clay.
Firing temperature, between 950-1020ºC.
Transparent glaze - PR 211 B
Composed of Frit.
The firing temperature varies between 980-1020ºC.
Satin transparent glaze - PR17
Composed of Frit.
Clear satin lead-free enamel.
The firing temperature varies between 980-1050ºC.
Calco-alkaline glaze - PR 1440 (FR 10)
Composed of fritte.
Lead-free transparent enamel with relatively high expansion.
Application Ceramic product for enamelling of white and red clay pieces with an expansion superior to the standard.
Admit to the decoration.
The firing interval is between 940 and 1000ºC.
Transparent boro calcium enamel - PR1430
Transparent and glossy enamel, lead-free.
Transparent expansion corrector enamel - PR14
It is a corrector, low dilatation.
Application Raw material in ceramics.
The use is very limited by its low expansion.
It can be added to certain enamels to reduce their dilatation.
Recommended firing temperature between 980-1050ºC.
Transparent enamel - PR 1000 (FR 8)
Composed of frit.
Transparent, lead-free and very melting email.
Raw material in the ceramic industry.
This is a basis for the development of lead-free enamels.
Recommended firing temperature between 850-1000°C.
Transparent glaze - NS20M
Composed of Frit.
Lead-free shiny transparent enamel.
For enamelling ceramic pieces in white clay.
Firing temperature between 980-1020ºC.
Mono lead silicate enamel - MONOPB
Composed of Frit.
Transparent, shiny and melting enamel.
With lead.
Matte transparent enamel - G 1005
Composed of Frit.
Transparent satin zinc and lead enamel.
Can be easily colored.
One must take into account the fact that zinc oxide can be bad to develop certain oxides dyes.
We recommend applying it for white paste and thin layer to avoid opalescences.
The firing temperature varies between 950-1000ºC.